Twin-roll casting of aluminum-steel clad strips

The results of experiments on twin-roll casting of aluminum-steel clad strips are presented. For the first time this energy-saving production technology for a clad material of this metals combination was implemented. Besides the experimental equipment and processing details, the results of metallographic, electron microprobe and transmission electron microscopy analysis of the aluminum-steel interface are shown. The pack rolling and deep-drawing tests of the twin-roll cast clad strips were performed to check their applicability for a further processing using plastic deformation. In addition adhesive strength of the bond was tested. The performed analysis have shown the formation of a continuous, thin and uniform layer of intermetallic phases on the materials interface of approx. 3 μm thickness having an adhesive strength over 70 MPa.